Sarafil MMTP46I series of Metalized Polyester film is suitable for Carton lamination applications. Modified surface
opposite to metalized surface of the film ensures good adhesion to solvent, water and UV based inks used in carton printing.
MICRON(GAUGE) |
10 (40) |
|
|
|
|
TYPE |
MMTP46I |
Metalised polyester film, coating outside |
|
|
|
|
|
|
|
PROPERTIES |
|
TEST |
UNIT |
10(40) |
|
|
|
METHOD |
|
MICRON |
|
|
|
|
|
(GAUGE) |
|
|
|
|
|
|
|
PROPERTIES |
|
|
|
|
|
|
|
|
|
|
|
OPTICAL DENSITY |
|
Polyplex |
|
2.2 |
|
|
|
Method |
|
|
|
|
|
|
|
|
NOMINAL THICKNESS |
Polyplex |
Micron |
10 |
|
|
|
Method |
|
|
|
|
|
|
|
|
|
|
|
|
Gauge |
40 |
|
|
|
|
|
|
|
YIELD |
|
Polyplex |
m2/kg |
71.4 |
|
|
|
Method |
|
|
|
|
|
|
|
|
|
|
|
|
in2/lb |
50400 |
|
|
|
|
|
|
MECHANICAL PROPERTIES |
|
|
|
|
|
|
|
|
TENSILE STRENGTH |
|
|
|
|
|
|
|
|
|
|
MD |
|
ASTM D-882 |
kg/cm2 |
2200 |
|
|
|
|
|
nbsp; |
|
|
|
|
kpsi |
31.5 |
|
|
|
|
|
|
|
TD |
|
ASTM D-882 |
kg/cm2 |
2300 |
|
|
|
|
|
|
|
|
|
|
kpsi |
32.9 |
|
|
|
|
|
|
|
ELONGATION AT BREAK |
|
|
|
|
|
|
|
|
|
|
MD |
|
ASTM D-882 |
% |
130 |
|
|
|
|
|
|
|
TD |
|
ASTM D-882 |
% |
125 |
|
|
|
|
|
|
|
THERMAL PROPERTIES |
|
|
|
|
|
|
|
HEAT SHRINKAGE (AT 150 DEG. C FOR 30 MIN) |
|
|
|
|
|
|
|
|
MD |
|
ASTM D- |
% |
2.0 |
|
|
|
1204 |
|
|
|
|
|
|
|
|
|
TD |
|
ASTM D- |
% |
0.2 |
|
|
|
1204 |
|
|
|
|
|
|
|
|
|
SURFACE PROPERTIES |
|
|
|
|
|
|
|
|
|
CO-EFFICIENT OF FRICTION, (A/B) |
|
|
|
|
|
|
|
|
|
STATIC |
|
ASTM D- |
|
0.65 |
|
|
|
1894 |
|
|
|
|
|
|
|
|
|
DYNAMIC |
|
ASTM D- |
|
0.60 |
|
|
|
1894 |
|
|
|
|
|
|
|
|
|
SURFACE TENSION |
|
|
|
|
|
|
|
|
|
|
|
COATED SIDE |
|
ASTM D- |
Dyne/cm |
42 |
|
|
|
2578 |
|
|
|
|
|
|
|
|
|
BARRIER PROPERTIES |
|
|
|
|
|
|
|
|
|
|
|
WVTR, 37.7 DEG 90% RH |
|
ASTM F- |
g/m2/day |
1.0 |
|
|
|
1249 |
|
|
|
|
|
|
|
|
|
OTR (23 ºC & 0% RH) |
|
ASTM D- |
cc/m2/day |
1.2 |
|
|
|
3985-95 |
|
|
|
|
|
|
|
|
|